5 Slip resistance
DIN 51097 (92)
Every Teuco product lives with water and for water: for us, it is vital that the materials used are safe and non-slip. Duralight
®
was tested
at the Bologna Ceramic Centre, which specialises in research and experimentation for the ceramic industry. The 0.5 cm thick 100x50 cm
slab of Duralight
®
was tested according to the international standard DIN 51097(92) “SLIP RESISTANCE”: Duralight
®
falls within the
A+B band, the same as generic shower rooms, swimming pools for children, bathtub perimeter zones and water access ladders,
where safety must be especially guaranteed.
Maintenance and cleaning of Teuco Duralight
®
surfaces.
Teuco Duralight
®
is easy to clean because it is uniform and compact. The instructions provided below are the result of experience
gained in the laboratory with respect to the most common circumstances found in the practical use of Duralight
®
products, which might
not, however, be able to solve problems caused by improper use. For circumstances other than those described in this document,
we suggest you seek further information from Teuco Technical Support.
Duralight
®
: easier to repair than polyester-based surfaces.
On polyester-based surfaces, repairs are more difficult because the colouring is often only superficial and not
throughout the product’s mass. Vigorous scrubbing may bring out a different colour at different depths.
Moreover, any retouching on polyester surfaces becomes even more obvious.
Cleaning and maintenance
Warnings
Detergents that contain alcohol, strong acids and acetones
must not be used to treat the Teuco Duralight
®
surface.
If this kind of product comes into contact with the material, we
recommend cleaning the surface immediately with plenty of water and
detergent to avoid the formation of permanent stains. Take care not to
use coloured detergents which could leave pigment residues.
Avoid contact between the material and products with high colouring
power such as nail varnish, hair dyes, self-tanning products, etc., and
oil-based products (hair oil and conditioner), because they could cause
permanent stains.
Do not use cloths or pads containing metal wire.
Recommended products
-
Soft cotton cloths of a “natural multi-purpose” type
-
Bathroom sponges (non abrasive)
-
Ammonia-based detergents
1
(e.g. LYSOFORM)
-
Slightly abrasive cream-based detergents
2
(e.g. CIF)
-
Descaling agents
3
(e.g. VIAKAL)
-
Bleach
4
Daily cleaning
Remove dirt residue with a wet cloth or sponge, using detergent.
Rinse with hot water and dry with a soft cloth.
Limescale residue
Remove limescale deposits with a cloth or a sponge, using a descaling
agent. In the case of tough deposits, repeat the operation, leaving the
descaling detergent to act for a maximum of 5 minutes.
Rinse with hot water and dry with a soft cloth.
Colouring substance residue
Remove stains with a cloth or a sponge, using a slightly abrasive
detergent. In the case of tough stains, repeat the operation using bleach.
Rinse with hot water and dry with a soft cloth.
Burns
Small burns and nicotine residues can be reduced/removed by rubbing
with a cloth or a sponge, using a slightly abrasive detergent or some
bleach.
Rinse with hot water and dry with a soft cloth.
Extraordinary cleaning
In order to maintain the initial colour of the material, we suggest, from
time to time, applying a solution composed of 3⁄4 bleach and 1⁄4 water,
leaving it to act for a maximum of 8 hours.
Rinse with hot water and dry with a soft cloth.
Restoration of the surface
If stains cannot be removed by the above methods, or if there are signs
of abrasion or superficial notches, the abrasive (Scotch-BriteTM) sponge
supplied (HARD abrasive sponge, 150 FEPA finish) should
be used.
- Matt surfaces
Rub down the surface with the abrasive (Scotch-BriteTM) sponge in a
sequence of circular movements, preferably dampening the sponge with
water.
- Gloss surfaces
After rubbing down with the abrasive (Scotch-BriteTM) sponge, the
treated surface must be polished with the aid of a polishing paste (polish)
and a soft cloth.
In the event of damage that cannot be repaired using the abrasive
(Scotch-BriteTM) sponge, contact Teuco Technical Support.
(1) - With a composition of no more than: 5% sodium tripolyphosphate, 5% alkyldimethylbenzylammonium chloride, 5% alkyl alcohol ethoxylate.
(2) - With a composition of no more than: 15% sodium alkyl benzene sulfonate, 5% alkyl alcohol ethoxylate.
(3) - With a composition of no more than: 5% non-ionic surfactants, 5% formic acid, 5% phosphoric acid.
(4) - Sodium hypochlorite (NaClO) in concentration of not more than 15%.
37
6 Brilliance and brightness
Greater brilliance and brightness are among the advantages of Duralight
®
. In particular, thanks to the Cold Cure manufacturing
process, the acrylic can be worked creating surfaces with a gloss and not just a matt finish. The gloss effect, which is not used
in standard production however, is obtained by pouring the liquid material into a mould with a glossy surface.
So for customers who choose Duralight
®
with a gloss finish, the maximum brightness is assured.
Surface Specular Reflection (Glossy) Test UNI 9149
This test measures the specular reflection of the surfaces by means of a Picogloss.
Glossy Test 60°
DLI F27 Cold Cure
Polyester-based
compound
36